Zinc paint 90% – 1 Litre

£39.22 (+VAT)

Corrosion protection with a high level of protection for iron and steel Application: For large surfaces that have not yet been painted For the repair of damaged galvanised parts, corrosion protection for weld seams, and the cold galvanisation of metal surfaces in mechanical engineering, plant engineering and bodywork Can be painted with synthetic resin paint…

Description

Corrosion protection with a high level of protection for iron and steel

Application:

For large surfaces that have not yet been painted
For the repair of damaged galvanised parts, corrosion protection for weld seams, and the cold galvanisation of metal surfaces in mechanical engineering, plant engineering and bodywork
Can be painted with synthetic resin paint
Cannot be painted with 2K paints
Theoretical yield: 8 m²/l or 3.4 m² with a coat thickness of 50 µm
Apply using a brush or roller
Ventilation time: at least 10 minutes before any oven drying
Quick drying
Temperature-resistant to approx. 400°C
Colour: matt
Specific weight: 2.16–2.30 kg/l
Chromate-free and lead-free
Pre-treatment of iron and steel surfaces: sand blasting
Dust-dry after 20–30 minutes (at 20°C)
Set to touch after 50–60 minutes (at 20°C)
Hardened after 6 hours (at 20°C)
Can be coated after 12 hours (at 20°C)
Final hardness after 3–4 days (at 20°C)
Lower temperatures result in longer drying times